In Situ Observation of Domain Structure of Molybdates Gadolinum Single Crystal by Synchrotron X-Ray Topography

Get Citation
YUAN Qing-Xi, XU Jun, PAN Shou-Kui, HUANG Wan-Xia, TIAN Yu-Lian and JIANG Jian-Hua. In Situ Observation of Domain Structure of Molybdates Gadolinum Single Crystal by Synchrotron X-Ray Topography[J]. Chinese Physics C, 2001, 25(S1): 116-120.
YUAN Qing-Xi, XU Jun, PAN Shou-Kui, HUANG Wan-Xia, TIAN Yu-Lian and JIANG Jian-Hua. In Situ Observation of Domain Structure of Molybdates Gadolinum Single Crystal by Synchrotron X-Ray Topography[J]. Chinese Physics C, 2001, 25(S1): 116-120. shu
Milestone
Received: 1900-01-01
Revised: 1900-01-01
Article Metric

Article Views(2417)
PDF Downloads(503)
Cited by(0)
Policy on re-use
To reuse of subscription content published by CPC, the users need to request permission from CPC, unless the content was published under an Open Access license which automatically permits that type of reuse.
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Email This Article

Title:
Email:

In Situ Observation of Domain Structure of Molybdates Gadolinum Single Crystal by Synchrotron X-Ray Topography

    Corresponding author: YUAN Qing-Xi,
  • Shanghai Institute of Optics and Fine Mechanics,CAS,Shanghai 201800,ChinaLaboratory of Solid State Microstructure,Nanjing University,Nanjing 210008,China1 Institute of High Energy Physics,CAS,Beijing 100039,China

Abstract: The domain structure of Gd2(MoO4)3 single crystal grown by Czochralski technique was observed first using a polarizing microscope,then using the Synchrotron X-ray topography under the conditions that the temperature of the crystal piece was increased from room temperature to 200°C and to applied DC voltage was varied from 0V to 4400V.The experiment results show that there are ferroelectric and ferroelastic domains in the crystal,but these two kinds of domains all disappeared when the temperature was increased above Curie temperature and could be transformed to a single domain when the applied DC voltage was high enough.This experimental results shows us that it is possible to make periodically poled Gd2(MoO4)3 crystal,though the presence of ferroelastic domain.