Cavity swelling of RAFM steel under 792 MeV Ar-ions irradiation at 773 K

Get Citation
SHEN Tie-Long, WANG Zhi-Guang, YAO Cun-Feng, SUN Jian-Rong, WEI Kong-Fang, ZHU Ya-Bin, PANG Li-Long, CUI Ming-Huan, LI Yuan-Fei, MA Yi-Zhun, SHENG Yan-Bin and GOU Jie. Cavity swelling of RAFM steel under 792 MeV Ar-ions irradiation at 773 K[J]. Chinese Physics C, 2013, 37(8): 088201. doi: 10.1088/1674-1137/37/8/088201
SHEN Tie-Long, WANG Zhi-Guang, YAO Cun-Feng, SUN Jian-Rong, WEI Kong-Fang, ZHU Ya-Bin, PANG Li-Long, CUI Ming-Huan, LI Yuan-Fei, MA Yi-Zhun, SHENG Yan-Bin and GOU Jie. Cavity swelling of RAFM steel under 792 MeV Ar-ions irradiation at 773 K[J]. Chinese Physics C, 2013, 37(8): 088201.  doi: 10.1088/1674-1137/37/8/088201 shu
Milestone
Received: 2012-07-26
Revised: 1900-01-01
Article Metric

Article Views(2075)
PDF Downloads(181)
Cited by(0)
Policy on re-use
To reuse of subscription content published by CPC, the users need to request permission from CPC, unless the content was published under an Open Access license which automatically permits that type of reuse.
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Email This Article

Title:
Email:

Cavity swelling of RAFM steel under 792 MeV Ar-ions irradiation at 773 K

    Corresponding author: WANG Zhi-Guang,

Abstract: China reduced-activation ferritic/martensitic steel is irradiated at 773 K with 792 MeV Ar-ions to fluences of 2.3×1020 and 4.6× 1020 ions/m2, respectively. The variation of the microstructures of the Reduced-activation ferritic/martensitic (RAFM) steel samples with the Ar-ion penetration depth is investigated using a transmission electron microscope (TEM). From analyses of the microstructure changes along with the Ar-ions penetrating depth, it is found that high-density cavities form in the peak damage region. The average size and the number density of the cavities depend strongly on the damage level and Ar-atom concentration. Swelling due to the formation of cavities increases significantly with an increased damage level, and the existence of deposited Ar-atoms also enhances the growth of the average size of the cavities. The effect of atom displacements and Ar-atoms on the swelling of the RAFM steel under high energy Ar-ion irradiation is discussed briefly.